杜邦高性能聚合物SK603 NC010/20%的玻璃纤维填充

杜邦高性能聚合物Crastin®SK603 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；聚对苯二甲酸丁二醇酯（PBT），20%的玻璃纤维填充 材料说明：20%玻璃纤维增强聚对苯二甲酸丁二醇酯 Crastin SK603 NC010是20%玻璃纤维增强聚对苯二甲酸乙二醇酯树脂注塑成型润滑。
 物性表：

 
Physical Properties Metric English Comments
Density  1.26 g/cc 0.0455 lb/in³  
  1.45 g/cc 0.0524 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   80120 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 80120 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  94280 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 94280 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  112300 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 112300 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  238200 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 238200 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  293100 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 293100 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  362400 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 362400 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  125 MPa 18100 psi ISO 527-1/-2
Tensile Stress   21.6 MPa
@Strain 0.300 %,
Temperature 23.0 °C		 3130 psi
@Strain 0.300 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  73.5 MPa
@Strain 1.20 %,
Temperature 23.0 °C		 10700 psi
@Strain 1.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  105 MPa
@Strain 2.10 %,
Temperature 23.0 °C		 15200 psi
@Strain 2.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  115 MPa
@Strain 3.30 %,
Temperature 23.0 °C		 16700 psi
@Strain 3.30 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.152 %,
Time 36000 sec		 1450 psi
@Strain 0.152 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.179 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.179 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.286 %,
Time 3600 sec		 2900 psi
@Strain 0.286 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  30.0 MPa
@Strain 0.510 %,
Time 360000 sec		 4350 psi
@Strain 0.510 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.975 %,
Time 3.60e+6 sec		 7250 psi
@Strain 0.975 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.785 %,
Time 36000 sec		 7250 psi
@Strain 0.785 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.745 %,
Time 3600 sec		 7250 psi
@Strain 0.745 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  60.0 MPa
@Strain 1.09 %,
Time 360000 sec		 8700 psi
@Strain 1.09 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  3.2 % 3.2 % ISO 527-1/-2
Tensile Modulus  7.40 GPa 1070 ksi ISO 527-1/-2
  2.20 GPa
@Temperature 150 °C		 319 ksi
@Temperature 302 °F		 ISO 11403-1 -2
  3.684 GPa
@Temperature 60.0 °C		 534.3 ksi
@Temperature 140 °F		 ISO 11403-1 -2
  7.35 GPa
@Temperature -20.0 °C		 1070 ksi
@Temperature -4.00 °F		 ISO 11403-1 -2
Flexural Strength  180 MPa 26100 psi ISO 178
Flexural Modulus  6.20 GPa 899 ksi ISO 178
Shear Modulus   0.365 GPa
@Temperature 160 °C		 52.9 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.471 GPa
@Temperature 120 °C		 68.3 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.704 GPa
@Temperature 70.0 °C		 102 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.54 GPa
@Temperature 20.0 °C		 223 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.66 GPa
@Temperature -20.0 °C		 241 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.77 GPa
@Temperature -50.0 °C		 257 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   4.625 GPa
@Strain 2.40 %,
Temperature 23.0 °C		 670.8 ksi
@Strain 2.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  6.125 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 888.4 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  7.20 GPa
@Strain 0.300 %,
Temperature 23.0 °C		 1040 ksi
@Strain 0.300 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  60.0 kJ/m² 28.6 ft-lb/in² ISO 180/1U
  60.0 kJ/m²
@Temperature -30.0 °C		 28.6 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  6.00 J/cm² 28.6 ft-lb/in² ISO 179/1eU
  5.50 J/cm²
@Temperature -30.0 °C		 26.2 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² ISO 179/1eA
  0.900 J/cm²
@Temperature -30.0 °C		 4.28 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   3090 MPa
@Pressure 50.0 MPa,
Temperature 60.0 °C		 448000 psi
@Pressure 7250 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3090 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 448000 psi
@Pressure 5800 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3100 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 450000 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3110 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 451000 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3119.7 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 452480 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  6060 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 879000 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6310 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 915000 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6540 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 949000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6710 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 973000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6840 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 992000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6970.9 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.0110e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6980 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.01e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6990 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.01e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7200 MPa
@Time 3600 sec		 1.04e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   2480 MPa
@Pressure 50.0 MPa,
Temperature 60.0 °C		 359000 psi
@Pressure 7250 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2480 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 360000 psi
@Pressure 5800 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2480 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 360000 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2490 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 361000 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2500 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 362000 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3940 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 572000 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4490 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 651000 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4880 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 708000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5130 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 744000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5320 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 771000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5460 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 792000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5560 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 806000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5590 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 810000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5600 MPa
@Time 3.60e+6 sec		 812000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.6
@Frequency 1.00e+6 Hz		 3.6
@Frequency 1.00e+6 Hz		 IEC 60250
  4.2
@Frequency 100 Hz		 4.2
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  29.0 kV/mm 737 kV/in IEC 60243-1
Dissipation Factor   0.0021
@Frequency 100 Hz		 0.0021
@Frequency 100 Hz		 IEC 60250
  0.019
@Frequency 1.00e+6 Hz		 0.019
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  400 V 400 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  40.0 µm/m-°C 22.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.86 J/g-°C 0.445 BTU/lb-°F  
Thermal Conductivity  0.250 W/m-K 1.74 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  204 °C 399 °F ISO 75-1/-2
Vicat Softening Point  210 °C 410 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  28 mm/min
@Thickness 1.00 mm		 1.1 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Emission of organic compounds 140 µgC/g VDA 277
Odour class 3 VDA 270
Part Marking Code >PBT-GF20< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF20  
UL recognition UL


图：



上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40919.html

免责声明: 本文 杜邦高性能聚合物SK603 NC010/20%的玻璃纤维填充 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4