杜邦高性能聚合物sk608 bk509/50%的玻璃纤维填充

杜邦高性能聚合物Crastin®sk608 bk509聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；聚对苯二甲酸丁二醇酯（PBT），50%的玻璃纤维填充 材料说明：45%玻璃纤维增强聚对苯二甲酸丁二醇酯 Crastin sk608 bk509是注塑成型的45%玻璃纤维增强聚对苯二甲酸乙二醇酯树脂润滑。
 物性表：

 
Physical Properties Metric English Comments
Density  1.47 g/cc 0.0531 lb/in³  
  1.66 g/cc 0.0600 lb/in³ ISO 1183
Water Absorption  0.30 %
@Thickness 2.00 mm		 0.30 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.100 %
@Thickness 2.00 mm		 0.100 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  140 MPa 20300 psi ISO 527-1/-2
Tensile Stress   18.7 MPa
@Strain 0.270 %,
Temperature 90.0 °C		 2710 psi
@Strain 0.270 %,
Temperature 194 °F		 ISO 11403-1 -2
  20.51 MPa
@Strain 0.150 %,
Temperature 23.0 °C		 2975 psi
@Strain 0.150 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  21.01 MPa
@Strain 0.210 %,
Temperature 40.0 °C		 3047 psi
@Strain 0.210 %,
Temperature 104 °F		 ISO 11403-1 -2
  43.69 MPa
@Strain 0.800 %,
Temperature 90.0 °C		 6337 psi
@Strain 0.800 %,
Temperature 194 °F		 ISO 11403-1 -2
  59.23 MPa
@Strain 1.42 %,
Temperature 90.0 °C		 8591 psi
@Strain 1.42 %,
Temperature 194 °F		 ISO 11403-1 -2
  65.6 MPa
@Strain 0.750 %,
Temperature 40.0 °C		 9510 psi
@Strain 0.750 %,
Temperature 104 °F		 ISO 11403-1 -2
  67.39 MPa
@Strain 2.03 %,
Temperature 90.0 °C		 9774 psi
@Strain 2.03 %,
Temperature 194 °F		 ISO 11403-1 -2
  71.91 MPa
@Strain 0.580 %,
Temperature 23.0 °C		 10430 psi
@Strain 0.580 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  91.43 MPa
@Strain 1.30 %,
Temperature 40.0 °C		 13260 psi
@Strain 1.30 %,
Temperature 104 °F		 ISO 11403-1 -2
  108.1 MPa
@Strain 1.00 %,
Temperature 23.0 °C		 15680 psi
@Strain 1.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  129.8 MPa
@Strain 1.43 %,
Temperature 23.0 °C		 18830 psi
@Strain 1.43 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Elongation at Break  2.0 % 2.0 % ISO 527-1/-2
Tensile Modulus  14.2 GPa 2060 ksi ISO 527-1/-2
Flexural Strength  210 MPa 30500 psi ISO 178
Flexural Modulus  13.3 GPa 1930 ksi ISO 178
Shear Modulus   0.6417 GPa
@Temperature 160 °C		 93.07 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.812 GPa
@Temperature 120 °C		 118 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  1.167 GPa
@Temperature 70.0 °C		 169.2 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  2.263 GPa
@Temperature 20.0 °C		 328.3 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  2.438 GPa
@Temperature -20.0 °C		 353.7 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  2.578 GPa
@Temperature -50.0 °C		 374.0 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   6.275 GPa
@Strain 1.60 %,
Temperature 40.0 °C		 910.1 ksi
@Strain 1.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  8.75 GPa
@Strain 0.750 %,
Temperature 40.0 °C		 1270 ksi
@Strain 0.750 %,
Temperature 104 °F		 ISO 11403-1 -2
  10.0 GPa
@Strain 0.210 %,
Temperature 40.0 °C		 1450 ksi
@Strain 0.210 %,
Temperature 104 °F		 ISO 11403-1 -2
  10.193 GPa
@Strain 1.14 %,
Temperature 23.0 °C		 1478.4 ksi
@Strain 1.14 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  12.4 GPa
@Strain 0.580 %,
Temperature 23.0 °C		 1800 ksi
@Strain 0.580 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  13.7 GPa
@Strain 0.150 %,
Temperature 23.0 °C		 1980 ksi
@Strain 0.150 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  10.0 kJ/m² 4.76 ft-lb/in² ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Charpy Impact Unnotched  5.50 J/cm² 26.2 ft-lb/in² ISO 179/1eU
  6.50 J/cm²
@Temperature -30.0 °C		 30.9 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm² 4.76 ft-lb/in² ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Dielectric Constant   3.9
@Frequency 1.00e+6 Hz		 3.9
@Frequency 1.00e+6 Hz		 IEC 60250
  4.1
@Frequency 100 Hz		 4.1
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  32.0 kV/mm 813 kV/in IEC 60243-1
Dissipation Factor   0.0038
@Frequency 100 Hz		 0.0038
@Frequency 100 Hz		 IEC 60250
  0.013
@Frequency 1.00e+6 Hz		 0.013
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  475 V 475 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  20.0 µm/m-°C 11.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  80.0 µm/m-°C 44.4 µin/in-°F ISO 11359-1/-2
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  222 °C 432 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  207 °C 405 °F ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  20 % 20 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-GF45< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF45  
UL recognition UL

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40922.html

免责声明: 本文 杜邦高性能聚合物sk608 bk509/50%的玻璃纤维填充 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4