LCP 7244 材料说明：泽尼特7244是一个40% glasslmineral增强液晶聚合物树脂具有较高的热变形温度295c，高流动性和良好的平整度。”
LCP 7244 性能参数表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.40 % | 1.40 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 11.3 GPa | 1640 ksi | ISO 178 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 41.0 µm/m-°C | 22.8 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 295 °C | 563 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
|