LCP 7755 材料说明：泽尼特7755注塑55%玻璃/矿物增强液晶聚合物树脂。它具有良好的耐冲击性、耐高温性，适合于不同行业的应用。
LCP 7755 参数说明表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.00 % | 1.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 17.6 GPa | 2550 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C | 5.00 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C | 590 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|