  4. 杜邦高性能聚合物dym350bk/良好的耐冲击性

杜邦高性能聚合物dym350bk/良好的耐冲击性

杜邦高性能聚合物Hytrel TPC-ET +®dym350bk PBT 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；聚酯热塑性弹性体 材质说明：聚酯弹性体材料，具有良好的耐冲击性，为气囊门应用开发
 物性表：

 
Physical Properties Metric English Comments
Density  1.00 g/cc 0.0361 lb/in³  
  1.18 g/cc 0.0426 lb/in³ ISO 1183
Water Absorption  0.60 %
@Thickness 2.00 mm		 0.60 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Water Absorption at Saturation  0.60 % 0.60 % Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow  0.013 cm/cm 0.013 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.014 cm/cm 0.014 in/in ISO 294-4 2577
Melt Flow   14 g/10 min
@Load 2.16 kg,
Temperature 240 °C		 14 g/10 min
@Load 4.76 lb,
Temperature 464 °F		 cm³/10min; ISO 1133
  15 g/10 min
@Load 2.16 kg,
Temperature 240 °C		 15 g/10 min
@Load 4.76 lb,
Temperature 464 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Shore D  50 50 15s; ISO 868
  <= 55 <= 55 ISO 868
Tensile Strength at Break  35.0 MPa 5080 psi ISO 527-1/-2
Tensile Stress   10.5 MPa
@Strain 5.00 %		 1520 psi
@Strain 5.00 %		 ISO 527-1/-2
  13.0 MPa
@Strain 10.0 %		 1890 psi
@Strain 10.0 %		 ISO 527-1/-2
  16.0 MPa
@Strain 50.0 %		 2320 psi
@Strain 50.0 %		 ISO 527-1/-2
  3.65 MPa
@Strain 7.23 %,
Temperature 120 °C		 529 psi
@Strain 7.23 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  3.94 MPa
@Strain 5.00 %,
Temperature 80.0 °C		 571 psi
@Strain 5.00 %,
Temperature 176 °F		 TPE; ISO 11403-1 -2
  4.64 MPa
@Strain 7.63 %,
Temperature 100 °C		 673 psi
@Strain 7.63 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  5.13 MPa
@Strain 7.75 %,
Temperature 90.0 °C		 744 psi
@Strain 7.75 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  5.38 MPa
@Strain 18.24 %,
Temperature 120 °C		 780 psi
@Strain 18.24 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  5.92 MPa
@Strain 28.56 %,
Temperature 120 °C		 859 psi
@Strain 28.56 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.17 MPa
@Strain 38.88 %,
Temperature 120 °C		 895 psi
@Strain 38.88 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.32 MPa
@Strain 49.89 %,
Temperature 120 °C		 917 psi
@Strain 49.89 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.46 MPa
@Strain 63.66 %,
Temperature 120 °C		 937 psi
@Strain 63.66 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.61 MPa
@Strain 78.11 %,
Temperature 120 °C		 959 psi
@Strain 78.11 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.66 MPa
@Strain 18.26 %,
Temperature 100 °C		 966 psi
@Strain 18.26 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  6.75 MPa
@Strain 91.87 %,
Temperature 120 °C		 979 psi
@Strain 91.87 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  6.92 MPa
@Strain 106.32 %,
Temperature 120 °C		 1000 psi
@Strain 106.32 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  7.19 MPa
@Strain 127.66 %,
Temperature 120 °C		 1040 psi
@Strain 127.66 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  7.30 MPa
@Strain 15.0 %,
Temperature 80.0 °C		 1060 psi
@Strain 15.0 %,
Temperature 176 °F		 TPE; ISO 11403-1 -2
  7.32 MPa
@Strain 28.88 %,
Temperature 100 °C		 1060 psi
@Strain 28.88 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  7.37 MPa
@Strain 18.54 %,
Temperature 90.0 °C		 1070 psi
@Strain 18.54 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  7.38 MPa
@Strain 7.86 %,
Temperature 60.0 °C		 1070 psi
@Strain 7.86 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  7.41 MPa
@Strain 141.42 %,
Temperature 120 °C		 1070 psi
@Strain 141.42 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  7.61 MPa
@Strain 40.16 %,
Temperature 100 °C		 1100 psi
@Strain 40.16 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  7.71 MPa
@Strain 159.31 %,
Temperature 120 °C		 1120 psi
@Strain 159.31 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  7.77 MPa
@Strain 50.78 %,
Temperature 100 °C		 1130 psi
@Strain 50.78 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  7.93 MPa
@Strain 65.39 %,
Temperature 100 °C		 1150 psi
@Strain 65.39 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  8.07 MPa
@Strain 29.33 %,
Temperature 90.0 °C		 1170 psi
@Strain 29.33 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  8.09 MPa
@Strain 79.33 %,
Temperature 100 °C		 1170 psi
@Strain 79.33 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  8.21 MPa
@Strain 184.09 %,
Temperature 120 °C		 1190 psi
@Strain 184.09 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  8.26 MPa
@Strain 93.93 %,
Temperature 100 °C		 1200 psi
@Strain 93.93 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  8.36 MPa
@Strain 40.11 %,
Temperature 90.0 °C		 1210 psi
@Strain 40.11 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  8.45 MPa
@Strain 108.54 %,
Temperature 100 °C		 1230 psi
@Strain 108.54 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  8.50 MPa
@Strain 5.00 %,
Temperature 23.0 °C		 1230 psi
@Strain 5.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.53 MPa
@Strain 50.9 %,
Temperature 90.0 °C		 1240 psi
@Strain 50.9 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  8.64 MPa
@Strain 30.0 %,
Temperature 80.0 °C		 1250 psi
@Strain 30.0 %,
Temperature 176 °F		 TPE; ISO 11403-1 -2
  8.64 MPa
@Strain 5.00 %,
Temperature 0.000 °C		 1250 psi
@Strain 5.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  8.70 MPa
@Strain 65.06 %,
Temperature 90.0 °C		 1260 psi
@Strain 65.06 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  8.76 MPa
@Strain 129.78 %,
Temperature 100 °C		 1270 psi
@Strain 129.78 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  8.86 MPa
@Strain 212.3 %,
Temperature 120 °C		 1290 psi
@Strain 212.3 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  8.86 MPa
@Strain 79.22 %,
Temperature 90.0 °C		 1290 psi
@Strain 79.22 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  9.01 MPa
@Strain 144.39 %,
Temperature 100 °C		 1310 psi
@Strain 144.39 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  9.07 MPa
@Strain 94.05 %,
Temperature 90.0 °C		 1320 psi
@Strain 94.05 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  9.20 MPa
@Strain 45.0 %,
Temperature 80.0 °C		 1330 psi
@Strain 45.0 %,
Temperature 176 °F		 TPE; ISO 11403-1 -2
  9.24 MPa
@Strain 108.21 %,
Temperature 90.0 °C		 1340 psi
@Strain 108.21 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  9.36 MPa
@Strain 162.31 %,
Temperature 100 °C		 1360 psi
@Strain 162.31 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  9.57 MPa
@Strain 8.12 %,
Temperature 40.0 °C		 1390 psi
@Strain 8.12 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  9.59 MPa
@Strain 129.78 %,
Temperature 90.0 °C		 1390 psi
@Strain 129.78 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  9.73 MPa
@Strain 247.4 %,
Temperature 120 °C		 1410 psi
@Strain 247.4 %,
Temperature 248 °F		 TPE; ISO 11403-1 -2
  9.85 MPa
@Strain 144.61 %,
Temperature 90.0 °C		 1430 psi
@Strain 144.61 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  9.91 MPa
@Strain 187.53 %,
Temperature 100 °C		 1440 psi
@Strain 187.53 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  10.12 MPa
@Strain 18.8 %,
Temperature 60.0 °C		 1468 psi
@Strain 18.8 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  10.19 MPa
@Strain 162.14 %,
Temperature 90.0 °C		 1478 psi
@Strain 162.14 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  10.61 MPa
@Strain 216.08 %,
Temperature 100 °C		 1539 psi
@Strain 216.08 %,
Temperature 212 °F		 TPE; ISO 11403-1 -2
  10.76 MPa
@Strain 187.76 %,
Temperature 90.0 °C		 1561 psi
@Strain 187.76 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  10.9 MPa
@Strain 30.42 %,
Temperature 60.0 °C		 1580 psi
@Strain 30.42 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.14 MPa
@Strain 41.35 %,
Temperature 60.0 °C		 1616 psi
@Strain 41.35 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.25 MPa
@Strain 52.29 %,
Temperature 60.0 °C		 1632 psi
@Strain 52.29 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.38 MPa
@Strain 67.33 %,
Temperature 60.0 °C		 1651 psi
@Strain 67.33 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.46 MPa
@Strain 216.08 %,
Temperature 90.0 °C		 1662 psi
@Strain 216.08 %,
Temperature 194 °F		 TPE; ISO 11403-1 -2
  11.52 MPa
@Strain 82.36 %,
Temperature 60.0 °C		 1671 psi
@Strain 82.36 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.7 MPa
@Strain 97.4 %,
Temperature 60.0 °C		 1700 psi
@Strain 97.4 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  11.9 MPa
@Strain 112.44 %,
Temperature 60.0 °C		 1730 psi
@Strain 112.44 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  12.26 MPa
@Strain 134.99 %,
Temperature 60.0 °C		 1778 psi
@Strain 134.99 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  12.27 MPa
@Strain 19.41 %,
Temperature 40.0 °C		 1780 psi
@Strain 19.41 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  12.52 MPa
@Strain 149.35 %,
Temperature 60.0 °C		 1816 psi
@Strain 149.35 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  12.92 MPa
@Strain 168.49 %,
Temperature 60.0 °C		 1874 psi
@Strain 168.49 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  12.96 MPa
@Strain 30.71 %,
Temperature 40.0 °C		 1880 psi
@Strain 30.71 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.18 MPa
@Strain 8.61 %,
Temperature 23.0 °C		 1912 psi
@Strain 8.61 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  13.19 MPa
@Strain 42.0 %,
Temperature 40.0 °C		 1913 psi
@Strain 42.0 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.27 MPa
@Strain 53.3 %,
Temperature 40.0 °C		 1925 psi
@Strain 53.3 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.3 MPa
@Strain 5.00 %,
Temperature -30.0 °C		 1930 psi
@Strain 5.00 %,
Temperature -22.0 °F		 ISO 11403-1 -2
  13.36 MPa
@Strain 68.83 %,
Temperature 40.0 °C		 1938 psi
@Strain 68.83 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.48 MPa
@Strain 83.66 %,
Temperature 40.0 °C		 1955 psi
@Strain 83.66 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.55 MPa
@Strain 194.46 %,
Temperature 60.0 °C		 1965 psi
@Strain 194.46 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  13.6 MPa
@Strain 5.00 %,
Temperature -40.0 °C		 1970 psi
@Strain 5.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  13.63 MPa
@Strain 99.19 %,
Temperature 40.0 °C		 1977 psi
@Strain 99.19 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  13.7 MPa
@Strain 20.0 %,
Temperature 23.0 °C		 1990 psi
@Strain 20.0 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  13.81 MPa
@Strain 114.1 %,
Temperature 40.0 °C		 2003 psi
@Strain 114.1 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  14.15 MPa
@Strain 137.31 %,
Temperature 40.0 °C		 2052 psi
@Strain 137.31 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  14.4 MPa
@Strain 152.13 %,
Temperature 40.0 °C		 2090 psi
@Strain 152.13 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  14.4 MPa
@Strain 224.53 %,
Temperature 60.0 °C		 2090 psi
@Strain 224.53 %,
Temperature 140 °F		 TPE; ISO 11403-1 -2
  14.5 MPa
@Strain 35.0 %,
Temperature 23.0 °C		 2100 psi
@Strain 35.0 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  14.78 MPa
@Strain 171.19 %,
Temperature 40.0 °C		 2144 psi
@Strain 171.19 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  15.43 MPa
@Strain 198.2 %,
Temperature 40.0 °C		 2238 psi
@Strain 198.2 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  15.44 MPa
@Strain 20.08 %,
Temperature 23.0 °C		 2239 psi
@Strain 20.08 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  15.87 MPa
@Strain 7.71 %,
Temperature 0.000 °C		 2302 psi
@Strain 7.71 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  15.94 MPa
@Strain 32.38 %,
Temperature 23.0 °C		 2312 psi
@Strain 32.38 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  15.99 MPa
@Strain 72.55 %,
Temperature 23.0 °C		 2319 psi
@Strain 72.55 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.0 MPa
@Strain 44.68 %,
Temperature 23.0 °C		 2320 psi
@Strain 44.68 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.0 MPa
@Strain 56.15 %,
Temperature 23.0 °C		 2320 psi
@Strain 56.15 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.01 MPa
@Strain 88.12 %,
Temperature 23.0 °C		 2322 psi
@Strain 88.12 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.08 MPa
@Strain 104.52 %,
Temperature 23.0 °C		 2332 psi
@Strain 104.52 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.19 MPa
@Strain 120.1 %,
Temperature 23.0 °C		 2348 psi
@Strain 120.1 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.32 MPa
@Strain 228.38 %,
Temperature 40.0 °C		 2367 psi
@Strain 228.38 %,
Temperature 104 °F		 TPE; ISO 11403-1 -2
  16.41 MPa
@Strain 144.69 %,
Temperature 23.0 °C		 2380 psi
@Strain 144.69 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.59 MPa
@Strain 160.26 %,
Temperature 23.0 °C		 2406 psi
@Strain 160.26 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  16.8 MPa
@Strain 20.0 %,
Temperature 0.000 °C		 2440 psi
@Strain 20.0 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  16.84 MPa
@Strain 180.76 %,
Temperature 23.0 °C		 2442 psi
@Strain 180.76 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  17.27 MPa
@Strain 208.63 %,
Temperature 23.0 °C		 2505 psi
@Strain 208.63 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  18.03 MPa
@Strain 240.6 %,
Temperature 23.0 °C		 2615 psi
@Strain 240.6 %,
Temperature 73.4 °F		 TPE; ISO 11403-1 -2
  18.86 MPa
@Strain 3.86 %,
Temperature -40.0 °C		 2735 psi
@Strain 3.86 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  18.95 MPa
@Strain 18.25 %,
Temperature 0.000 °C		 2748 psi
@Strain 18.25 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.53 MPa
@Strain 7.70 %,
Temperature -20.0 °C		 2833 psi
@Strain 7.70 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  19.75 MPa
@Strain 29.6 %,
Temperature 0.000 °C		 2865 psi
@Strain 29.6 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.95 MPa
@Strain 40.15 %,
Temperature 0.000 °C		 2894 psi
@Strain 40.15 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.96 MPa
@Strain 79.89 %,
Temperature 0.000 °C		 2895 psi
@Strain 79.89 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.97 MPa
@Strain 93.68 %,
Temperature 0.000 °C		 2896 psi
@Strain 93.68 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.97 MPa
@Strain 65.29 %,
Temperature 0.000 °C		 2896 psi
@Strain 65.29 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  19.98 MPa
@Strain 50.69 %,
Temperature 0.000 °C		 2898 psi
@Strain 50.69 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  20.04 MPa
@Strain 108.28 %,
Temperature 0.000 °C		 2907 psi
@Strain 108.28 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  20.23 MPa
@Strain 130.18 %,
Temperature 0.000 °C		 2934 psi
@Strain 130.18 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  20.41 MPa
@Strain 144.78 %,
Temperature 0.000 °C		 2960 psi
@Strain 144.78 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  20.7 MPa
@Strain 162.62 %,
Temperature 0.000 °C		 3000 psi
@Strain 162.62 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  21.1 MPa
@Strain 20.0 %,
Temperature -30.0 °C		 3060 psi
@Strain 20.0 %,
Temperature -22.0 °F		 ISO 11403-1 -2
  21.19 MPa
@Strain 187.77 %,
Temperature 0.000 °C		 3073 psi
@Strain 187.77 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  21.93 MPa
@Strain 216.16 %,
Temperature 0.000 °C		 3181 psi
@Strain 216.16 %,
Temperature 32.0 °F		 TPE; ISO 11403-1 -2
  22.3 MPa
@Strain 20.0 %,
Temperature -40.0 °C		 3230 psi
@Strain 20.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  22.8 MPa
@Strain 35.0 %,
Temperature -30.0 °C		 3310 psi
@Strain 35.0 %,
Temperature -22.0 °F		 ISO 11403-1 -2
  23.64 MPa
@Strain 18.24 %,
Temperature -20.0 °C		 3429 psi
@Strain 18.24 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  24.7 MPa
@Strain 35.0 %,
Temperature -40.0 °C		 3580 psi
@Strain 35.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  24.93 MPa
@Strain 28.78 %,
Temperature -20.0 °C		 3616 psi
@Strain 28.78 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  25.53 MPa
@Strain 39.32 %,
Temperature -20.0 °C		 3703 psi
@Strain 39.32 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  25.82 MPa
@Strain 49.85 %,
Temperature -20.0 °C		 3745 psi
@Strain 49.85 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.0 MPa
@Strain 64.44 %,
Temperature -20.0 °C		 3770 psi
@Strain 64.44 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.03 MPa
@Strain 78.23 %,
Temperature -20.0 °C		 3775 psi
@Strain 78.23 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.07 MPa
@Strain 92.82 %,
Temperature -20.0 °C		 3781 psi
@Strain 92.82 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.24 MPa
@Strain 106.6 %,
Temperature -20.0 °C		 3806 psi
@Strain 106.6 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.66 MPa
@Strain 127.67 %,
Temperature -20.0 °C		 3867 psi
@Strain 127.67 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  26.93 MPa
@Strain 142.26 %,
Temperature -20.0 °C		 3906 psi
@Strain 142.26 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  27.1 MPa
@Strain 160.1 %,
Temperature -20.0 °C		 3930 psi
@Strain 160.1 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  27.56 MPa
@Strain 184.42 %,
Temperature -20.0 °C		 3997 psi
@Strain 184.42 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  28.19 MPa
@Strain 212.79 %,
Temperature -20.0 °C		 4089 psi
@Strain 212.79 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  28.79 MPa
@Strain 10.17 %,
Temperature -40.0 °C		 4176 psi
@Strain 10.17 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  29.54 MPa
@Strain 248.46 %,
Temperature -20.0 °C		 4284 psi
@Strain 248.46 %,
Temperature -4.00 °F		 TPE; ISO 11403-1 -2
  31.29 MPa
@Strain 15.78 %,
Temperature -40.0 °C		 4538 psi
@Strain 15.78 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  32.43 MPa
@Strain 21.4 %,
Temperature -40.0 °C		 4704 psi
@Strain 21.4 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.04 MPa
@Strain 99.26 %,
Temperature -40.0 °C		 4792 psi
@Strain 99.26 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.04 MPa
@Strain 114 %,
Temperature -40.0 °C		 4792 psi
@Strain 114 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.05 MPa
@Strain 27.01 %,
Temperature -40.0 °C		 4794 psi
@Strain 27.01 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.19 MPa
@Strain 85.94 %,
Temperature -40.0 °C		 4814 psi
@Strain 85.94 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.51 MPa
@Strain 34.72 %,
Temperature -40.0 °C		 4860 psi
@Strain 34.72 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.53 MPa
@Strain 76.11 %,
Temperature -40.0 °C		 4863 psi
@Strain 76.11 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.71 MPa
@Strain 42.44 %,
Temperature -40.0 °C		 4889 psi
@Strain 42.44 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.71 MPa
@Strain 68.4 %,
Temperature -40.0 °C		 4889 psi
@Strain 68.4 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.81 MPa
@Strain 49.46 %,
Temperature -40.0 °C		 4904 psi
@Strain 49.46 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
  33.84 MPa
@Strain 57.17 %,
Temperature -40.0 °C		 4908 psi
@Strain 57.17 %,
Temperature -40.0 °F		 TPE; ISO 11403-1 -2
Tensile Strength, Yield  15.0 MPa 2180 psi ISO 527-1/-2
Elongation at Break  >= 300 % >= 300 % ISO 527-1/-2
  600 % 600 % Nominal; ISO 527-1/-2
Elongation at Yield  43 % 43 % ISO 527-1/-2
Tensile Modulus  0.370 GPa 53.7 ksi ISO 527-1/-2
  0.553 GPa
@Temperature -30.0 °C		 80.2 ksi
@Temperature -22.0 °F		 ISO 11403-1 -2
Flexural Modulus  0.430 GPa 62.4 ksi ISO 178
Secant Modulus   0.020325 GPa
@Strain 40.0 %,
Temperature 100 °C		 2.9479 ksi
@Strain 40.0 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.022575 GPa
@Strain 40.0 %,
Temperature 80.0 °C		 3.2743 ksi
@Strain 40.0 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.0352 GPa
@Strain 20.0 %,
Temperature 100 °C		 5.11 ksi
@Strain 20.0 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.03965 GPa
@Strain 20.0 %,
Temperature 80.0 °C		 5.751 ksi
@Strain 20.0 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.0616 GPa
@Strain 5.00 %,
Temperature 100 °C		 8.93 ksi
@Strain 5.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.0685 GPa
@Strain 20.0 %,
Temperature 23.0 °C		 9.94 ksi
@Strain 20.0 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.0788 GPa
@Strain 5.00 %,
Temperature 80.0 °C		 11.4 ksi
@Strain 5.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.0840 GPa
@Strain 20.0 %,
Temperature 0.000 °C		 12.2 ksi
@Strain 20.0 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.1055 GPa
@Strain 20.0 %,
Temperature -30.0 °C		 15.30 ksi
@Strain 20.0 %,
Temperature -22.0 °F		 ISO 11403-1 -2
  0.1115 GPa
@Strain 20.0 %,
Temperature -40.0 °C		 16.17 ksi
@Strain 20.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.170 GPa
@Strain 5.00 %,
Temperature 23.0 °C		 24.7 ksi
@Strain 5.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.1728 GPa
@Strain 5.00 %,
Temperature 0.000 °C		 25.06 ksi
@Strain 5.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.266 GPa
@Strain 5.00 %,
Temperature -30.0 °C		 38.6 ksi
@Strain 5.00 %,
Temperature -22.0 °F		 ISO 11403-1 -2
  0.272 GPa
@Strain 5.00 %,
Temperature -40.0 °C		 39.5 ksi
@Strain 5.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Puncture Energy  40.0 J
@Load 336 kg		 29.5 ft-lb
@Load 742 lb		 ISO 6603-2
Tear Strength  105 kN/m 599 pli normal; ISO 34-1
  130 kN/m 742 pli parallel; ISO 34-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  5.00e+14 ohm 5.00e+14 ohm IEC 60093
Dielectric Constant   4.4
@Frequency 1.00e+6 Hz		 4.4
@Frequency 1.00e+6 Hz		 IEC 60250
  4.6
@Frequency 100 Hz		 4.6
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  20.0 kV/mm 508 kV/in IEC 60243-1
Dissipation Factor   0.0070
@Frequency 100 Hz		 0.0070
@Frequency 100 Hz		 IEC 60250
  0.023
@Frequency 1.00e+6 Hz		 0.023
@Frequency 1.00e+6 Hz		 IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  180 µm/m-°C 100 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  180 µm/m-°C 100 µin/in-°F ISO 11359-1/-2
Melting Point  222 °C 432 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  50.0 °C 122 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  40.0 °C 104 °F ISO 75-1/-2
Brittleness Temperature  -100 °C -148 °F ISO 974
Glass Transition Temp, Tg  -55.0 °C -67.0 °F 10°C/min; ISO 11357-1/-2
Flame Spread  23 mm/min
@Thickness 1.00 mm		 0.91 in/min
@Thickness 0.0394 in		 SE/B; ISO 3795 (FMVSS 302)
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Eff. thermal diffusivity 5.44E-08 m²/s  
Emission of organic compounds 2.7 µgC/g VDA 277
Odour class 5 VDA 270
Part Marking Code >TPC-ET+PBT< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification TPC-ET+PBT  
Special characteristics Light stabilised or stable to light

图：

 
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40949.html

免责声明: 本文 杜邦高性能聚合物dym350bk/良好的耐冲击性 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4