| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 | ||
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0700 % @Temperature 22.8 °C |
0.0700 % @Temperature 73.0 °F |
24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.170 % | 0.170 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0120 - 0.0160 cm/cm | 0.0120 - 0.0160 in/in | ISO 294-4 | ||
| 0.0250 - 0.0300 cm/cm | 0.0250 - 0.0300 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0120 - 0.0160 cm/cm | 0.0120 - 0.0160 in/in | ISO 294-4 | ||
| Melt Flow | 25.0 g/10 min | 25.0 g/10 min | ASTM D1238 | ||
| 18.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
18.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm3/10min]; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 79.0 | 79.0 | ISO 2039-2 | ||
| Tensile Strength, Yield | 59.3 MPa | 8600 psi | ASTM D638 | ||
| 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | |||
| Elongation at Break | 10.0 % | 10.0 % | |||
| 20.0 % | 20.0 % | ASTM D638 | |||
| Elongation at Yield | 3.00 % | 3.00 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 | ||
| 106 MPa | 15400 psi | ASTM D790 | |||
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 | ||
| 3.29 GPa | 477 ksi | ASTM D790 | |||
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU | ||
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature -30.0 °C |
2.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.00 @Frequency 1.00e+6 Hz |
3.00 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
| 3.50 @Frequency 1.00e+6 Hz |
3.50 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 3.60 @Frequency 100 Hz |
3.60 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| 27.6 kV/mm | 700 kV/in | short term; ASTM D149 | |||
| Dissipation Factor | 0.00470 @Frequency 100 Hz |
0.00470 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0100 @Frequency 1.00e+6 Hz |
0.0100 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| 0.0185 @Frequency 1.00e+6 Hz |
0.0185 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Arc Resistance | 96.0 sec | 96.0 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| 325 V | 325 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C | 42.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 328 °F | ASTM D648 | ||
| 165 °C | 329 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75-1, -2 | ||
| 70.0 °C | 158 °F | ASTM D648 | |||
| Vicat Softening Point | 190 °C | 374 °F | ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
||||
| Oxygen Index | 30.0 % | 30.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | cavity | ||
| 250 - 260 °C | 482 - 500 °F | hot runner | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 243 °C | 469 °F | ISO 294 | ||
| 235 - 255 °C | 455 - 491 °F | ||||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792-2 | ||||