| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Density of Compound | 1.32 g/cc | 0.0477 lb/in³ | |||
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 70.0 cm³/g | 70.0 cm³/g | ISO 307, 1157, 1628 | ||
| Melt Flow | 15.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
15.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
[cm3/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.60 J/cm² | 26.6 ft-lb/in² | ISO 179/1eU | ||
| 5.80 J/cm² @Temperature -30.0 °C |
27.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.10 @Frequency 1.00e+6 Hz |
4.10 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.40 @Frequency 100 Hz |
4.40 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00140 @Frequency 100 Hz |
0.00140 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0170 @Frequency 1.00e+6 Hz |
0.0170 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 | ||
| Specific Heat Capacity | 1.73 J/g-°C | 0.413 BTU/lb-°F | |||
| Thermal Conductivity | 0.171 W/m-K | 1.19 BTU-in/hr-ft²-°F | |||
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 225 °C | 437 °F | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.820 mm |
HB @Thickness 0.0323 in |
||||
| Oxygen Index | 20.0 % | 20.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 90.0 - 100 °C | 194 - 212 °F | cavity | ||
| 265 - 275 °C | 509 - 527 °F | hot runner | |||
| Feed Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 3 | 260 - 270 °C | 500 - 518 °F | |||
| Zone 4 | 260 - 270 °C | 500 - 518 °F | |||
| Die Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Melt Temperature | 270 °C | 518 °F | ISO 294 | ||
| 265 - 275 °C | 509 - 527 °F | ||||
| Mold Temperature | 90.0 °C | 194 °F | ISO 294 | ||
| Ejection Temperature | 220 °C | 428 °F | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |||
| Hold Pressure | 70.0 MPa | 10200 psi | ISO 294 | ||
| Screw Speed | 60.0 rpm @Diameter 55.0 mm |
60.0 rpm @Diameter 2.17 in |
|||
| 75.0 rpm @Diameter 40.0 mm |
75.0 rpm @Diameter 1.57 in |
||||
| 90.0 rpm @Diameter 25.0 mm |
90.0 rpm @Diameter 0.984 in |
||||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | fast | ||||
| Processing conditions acc. ISO | 7792 | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com