LCP C810 材料说明：说明：许多载货的特点。适用于线的宽度为10密耳的电镀。玻璃/矿物填充。
LCP C810 加工方法：注塑成型
LCP C810 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 133 MPa | 19300 psi | ISO 178 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
IEC 60250 |
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
IEC 60250 |
| 0.014 @Frequency 1e+6 Hz |
0.014 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.0 µm/m-°C @Temperature 20.0 °C |
12.8 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| Melting Point | 325 °C | 617 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 119 °C | 246 °F | ISO 75-1, -2 |
| Vicat Softening Point | 180 °C | 356 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | thickness h |