| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.090 % @Temperature 22.8 °C |
0.090 % @Temperature 73.0 °F |
24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ASTM D955 | ||
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 57.9 MPa @Temperature 22.8 °C |
8400 psi @Temperature 73.0 °F |
ASTM D638 | ||
| Tensile Stress | 30.0 MPa @Strain 50.0 % |
4350 psi @Strain 50.0 % |
50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A | ||
| 45 % @Temperature 22.8 °C |
45 % @Temperature 73.0 °F |
ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| 86.9 MPa @Temperature 22.8 °C |
12600 psi @Temperature 73.0 °F |
ASTM D790 | |||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| 2.74 GPa @Temperature 22.8 °C |
397 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 19.0 J/cm² @Temperature 30.0 °C |
90.4 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0014 @Frequency 100 Hz |
0.0014 @Frequency 100 Hz |
IEC 60250 | ||
| 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 | ||
| 160 °C | 320 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 | ||
| 55.0 °C | 131 °F | ASTM D648 | |||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||