LCP C550 加工方法：注塑成型
LCP C550 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | IEC 527 |
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 |
| Compressive Strength | 95.0 MPa | 13800 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 16.5 GPa | 2390 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 |
| Tensile Impact Strength | 50.0 kJ/m² | 23.8 ft-lb/in² | Notched; ASTM D1822 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+7 Hz |
3.7 @Frequency 1e+7 Hz |
|
| 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
IEC 250 | |
| Dissipation Factor | 0.0070 @Frequency 1e+7 Hz |
0.0070 @Frequency 1e+7 Hz |
|
| 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
IEC 250 | |
| Arc Resistance | 183 sec | 183 sec | |
| Comparative Tracking Index | 225 V | 225 V | IEC 112 |