| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 | ||
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 | ||
| 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 139 MPa | 20200 psi | 5mm/min; ISO 527-2/1A | ||
| 136.2 MPa @Temperature 22.8 °C |
19750 psi @Temperature 73.0 °F |
ASTM D638 | |||
| Elongation at Break | 2.7 % | 2.7 % | 5mm/min; ISO 527-2/1A | ||
| 2.7 % @Temperature 22.8 °C |
2.7 % @Temperature 73.0 °F |
ASTM D638 | |||
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| 211.3 MPa @Temperature 22.8 °C |
30650 psi @Temperature 73.0 °F |
ASTM D790 | |||
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 | ||
| 8.48 GPa @Temperature 22.8 °C |
1230 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO) | 11.7 kJ/m² | 5.57 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | ||
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | ISO 179/1eU | ||
 |
4.50 J/cm² @Temperature 30.0 °C |
21.4 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | ||
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA | ||
| 0.850 J/cm² @Temperature 30.0 °C |
4.04 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0022 @Frequency 100 Hz |
0.0022 @Frequency 100 Hz |
IEC 60250 | ||
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D648 | ||
| 225 °C | 437 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 | ||
| 207 °C | 405 °F | ASTM D648 | |||
| Vicat Softening Point | 220 °C | 428 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||