LCP v100p 类别：聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），空
LCP v100p 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | at 50% RH; ISO 62 |
| Moisture Vapor Transmission | 0.00787 cc-mm/m²-24hr-atm | 0.0200 cc-mil/100 in²-24hr-atm | at 38°C; DIN 53122-2 |
| Oxygen Transmission | 0.0236 cc-mm/m²-24hr-atm | 0.0600 cc-mil/100 in²-24hr-atm | 73°F, 100%RH; DIN 53380 part 3 |
| 0.0276 cc-mm/m²-24hr-atm | 0.0700 cc-mil/100 in²-24hr-atm | 73°F, 0% RH; DIN 53380 part 3 | |
| Carbon Dioxide Transmission | 0.0394 cc-mm/m²-24hr-atm | 0.100 cc-mil/100 in²-24hr-atm | 25°C, 0% RH; ISO/CD 15105-2C |
| 0.0512 cc-mm/m²-24hr-atm | 0.130 cc-mil/100 in²-24hr-atm | 25°C, 100% RH; ISO/CD 15105-2C | |
| Melt Flow | 9.0 g/10 min @Temperature 230 °C |
9.0 g/10 min @Temperature 446 °F |
I2, nominal; Internal |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 13.4 GPa | 1940 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 10.6 J/cm² | 50.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 7.70 J/cm² | 36.6 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 212 °C | 414 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-1, -2 |