LCP 1335MT 材料说明：说明：补充润滑性增强医用玻璃。建立了药品和主设备文件，符合美国药典VI级。
LCP 1335MT 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527-2/1A |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 280 °C | 536 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Middle Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Front Barrel Temperature | 285 - 295 °C | 545 - 563 °F | |
| Nozzle Temperature | 290 - 300 °C | 554 - 572 °F | |
| Melt Temperature | 285 - 295 °C | 545 - 563 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |