| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.97 g/cc | 0.0712 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 2.00 mm |
0.0010 in/in @Thickness 0.0787 in |
sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | |
| Melt Flow | 39.4 g/10 min @Load 2.16 kg, Temperature 250 °C |
39.4 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/2 |
| Elongation at Break | 1.1 % | 1.1 % | ISO 527-1/2 |
| Tensile Modulus | 11.4 GPa | 1650 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz |
5.0 @Frequency 1e+6 Hz |
IEC 60250 |
| 5.1 @Frequency 100 Hz |
5.1 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 150 V | 150 V | 100 drops value; IEC 60112 |
| 175 V | 175 V | Test Solution A CTI; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695 |
|