| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Post Shrinkage (5 h, 140°C) on 2 mm sheets with film gate at rim, mold temperature 80°C |
| 0.002 cm/cm @Thickness 2.00 mm |
0.002 in/in @Thickness 0.0787 in |
sheet with film gate at rim, mold temperature 80°C | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | Post Shrinkage (5 h, 140°C) on 2 mm sheets with film gate at rim, mold temperature 80°C |
| 0.011 cm/cm | 0.011 in/in | ||
| Melt Flow | 49.56 g/10 min @Load 2.16 kg, Temperature 250 °C |
49.56 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/2 |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527-1/2 |
| Tensile Modulus | 10.5 GPa | 1520 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695 |
|