| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 60 |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Viscosity Test | 94 cm³/g | 94 cm³/g | ISO 1628-5 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; acc. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; acc. ISO 2577 |
| Melt Flow | 40.5 g/10 min @Load 2.16 kg, Temperature 260 °C |
40.5 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 110 kJ/m² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| Charpy Impact Unnotched | 12.5 J/cm² @Temperature 23.0 °C |
59.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | Solution A; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1,-2 |
| Vicat Softening Point | 190 °C | 374 °F | 50 N; 50 °C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||
| Shrinkage | 0.200 % @Temperature 120 °C, Time 14400 sec |
0.200 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 150x105x3; acc. ISO 2577 |
| 0.200 % @Temperature 120 °C, Time 14400 sec |
0.200 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 150x105x3; acc. ISO 2577 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C |
4.00 - 8.00 hour @Temperature 248 °F |
|
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |