| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Melt Flow | 19 g/10 min | 19 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |
| Tensile Impact Strength | 50.0 kJ/m² | 23.8 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 48.0 kV/mm | 1220 kV/in | |
| Dissipation Factor | 0.0013 @Frequency 100 Hz |
0.0013 @Frequency 100 Hz |
|
| 0.0015 @Frequency 1e+6 Hz |
0.0015 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 200 V | 200 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| Vicat Softening Point | 137 °C | 279 °F | 50°C/hr/50 N |