gharda化学品g-paek™1230fc超高性能聚合物聚醚酮

gharda化学品g-paek™1230fc超高性能聚合物聚醚酮 类别:聚合物;热塑性的;聚酮;聚芳醚酮(PAEK),碳纤维填充 材料说明:产品详细信息:超高性能热塑性材料,10%碳纤维,10%聚四氟乙烯和10%石墨增强聚芳醚酮,半结晶颗粒,适合用于注塑,容易流动,黑色的颜色 适用范围:适用于高温应用,在承载力应用中需要较高强度和刚度。耐磨性优异。耐化学腐蚀的环境,适合用于医疗和食品接触的应用。
 物性表:

 
Physical Properties Metric English Comments
Specific Gravity  1.45 g/cc 1.45 g/cc  
Water Absorption  0.050 %
@Time 86400 sec
0.050 %
@Time 24.0 hour
 
Linear Mold Shrinkage, Flow  0.0011 cm/cm 0.0011 in/in 410°C nozzle, 220°C mold
Linear Mold Shrinkage, Transverse  0.0050 cm/cm 0.0050 in/in 410°C nozzle, 220°C mold
Crystallinity  40 % 40 % DSC
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  106 106 ASTM D785
Hardness, Shore D  91 91  
Tensile Strength at Break   45.0 MPa
@Temperature 250 °C
6530 psi
@Temperature 482 °F
ASTM D638
  55.0 MPa
@Temperature 200 °C
7980 psi
@Temperature 392 °F
ASTM D638
  80.0 MPa
@Temperature 150 °C
11600 psi
@Temperature 302 °F
ASTM D638
  120 MPa
@Temperature 100 °C
17400 psi
@Temperature 212 °F
ASTM D638
  130 - 135 MPa
@Temperature 23.0 °C
18900 - 19600 psi
@Temperature 73.4 °F
ASTM D638
  145 MPa
@Temperature -10.0 °C
21000 psi
@Temperature 14.0 °F
ASTM D638
  160 MPa
@Temperature -50.0 °C
23200 psi
@Temperature -58.0 °F
ASTM D638
Elongation at Break  1.5 - 2.0 % 1.5 - 2.0 % ASTM D638
Tensile Modulus  11.5 GPa 1670 ksi ASTM D638
Flexural Strength  210 MPa 30500 psi ASTM D790
Flexural Modulus  10.5 GPa 1520 ksi ASTM D790
Izod Impact, Notched  0.400 - 0.450 J/cm 0.749 - 0.843 ft-lb/in ASTM D256
Izod Impact, Unnotched  6.10 J/cm 11.4 ft-lb/in ASTM D256
 
Thermal Properties Metric English Comments
Melting Point  370 - 372 °C 698 - 702 °F DSC
Deflection Temperature at 1.8 MPa (264 psi)  368 °C 694 °F  
Glass Transition Temp, Tg  152 - 154 °C 306 - 309 °F DSC/onset
Flammability, UL94  V-0
@Thickness 0.800 mm
V-0
@Thickness 0.0315 in
 
 
Processing Properties Metric English Comments
Processing Temperature  390 - 425 °C 734 - 797 °F  
Nozzle Temperature  425 °C 797 °F  
Mold Temperature  200 - 220 °C 392 - 428 °F  
Drying Temperature  150 °C 302 °F  
Dry Time  4 - 6 hour 4 - 6 hour  
 
Descriptive Properties
Hopper/ Throat Temperature 60-80°C

0..

0..0..0..
上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41508.html

免责声明: 本文 gharda化学品g-paek™1230fc超高性能聚合物聚醚酮 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4