VICTREX PEEK®HT的™22gl30聚醚酮,30%玻璃纤维增强

VICTREX PEEK®HT的™22gl30聚醚酮,30%玻璃纤维增强 类别:聚合物;热塑性的;聚酮 材质说明:高性能热塑性材料,30%玻璃纤维增强聚醚酮(PEK),半结晶,颗粒成型,标准流程,符合美国FDA食品接触,颜色自然/米色。
 物性表:
 
Physical Properties Metric English Comments
Density  1.53 g/cc 0.0553 lb/in³ Crystalline; ISO 1183
Water Absorption at Saturation   0.50 %
@Temperature 23.0 °C
0.50 %
@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
  0.60 %
@Temperature 100 °C
0.60 %
@Temperature 212 °F
ISO 62-1
Viscosity  450000 cP
@Temperature 400 °C
450000 cP
@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in 360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse  0.0090 cm/cm 0.0090 in/in 395°C nozzle, 200°C tool; ISO 294-4
Spiral Flow  10.5 cm
@Thickness 1.00 mm
4.13 in
@Thickness 0.0394 in
395°C nozzle, 200°C tool
 
Mechanical Properties Metric English Comments
Hardness, Shore D  88
@Temperature 23.0 °C
88
@Temperature 73.4 °F
ISO 868
Tensile Strength at Break   55.0 MPa
@Temperature 275 °C
7980 psi
@Temperature 527 °F
ISO 527
  65.0 MPa
@Temperature 225 °C
9430 psi
@Temperature 437 °F
ISO 527
  75.0 MPa
@Temperature 175 °C
10900 psi
@Temperature 347 °F
ISO 527
  125 MPa
@Temperature 125 °C
18100 psi
@Temperature 257 °F
ISO 527
  200 MPa
@Temperature 23.0 °C
29000 psi
@Temperature 73.4 °F
ISO 527
Elongation at Break  2.9 %
@Temperature 23.0 °C
2.9 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus  12.0 GPa
@Temperature 23.0 °C
1740 ksi
@Temperature 73.4 °F
ISO 527
Flexural Strength   85.0 MPa
@Temperature 275 °C
12300 psi
@Temperature 527 °F
ISO 178
  120 MPa
@Temperature 175 °C
17400 psi
@Temperature 347 °F
ISO 178
  210 MPa
@Temperature 123 °C
30500 psi
@Temperature 253 °F
ISO 178
  290 MPa
@Temperature 23.0 °C
42100 psi
@Temperature 73.4 °F
ISO 178
Flexural Modulus  11.0 GPa
@Temperature 23.0 °C
1600 ksi
@Temperature 73.4 °F
ISO 178
Compressive Strength   50.0 MPa
@Temperature 250 °C
7250 psi
@Temperature 482 °F
ISO 604
  75.0 MPa
@Temperature 200 °C
10900 psi
@Temperature 392 °F
ISO 604
  180 MPa
@Temperature 120 °C
26100 psi
@Temperature 248 °F
ISO 604
  290 MPa
@Temperature 23.0 °C
42100 psi
@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO)  11.0 kJ/m²
@Temperature 23.0 °C
5.23 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO)  70.0 kJ/m²
@Temperature 23.0 °C
33.3 ft-lb/in²
@Temperature 73.4 °F
ISO 180/U
Charpy Impact Unnotched  7.00 J/cm²
@Temperature 23.0 °C
33.3 ft-lb/in²
@Temperature 73.4 °F
SO 179/1U
Charpy Impact, Notched  0.900 J/cm²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+16 ohm-cm 1.00e+16 ohm-cm IEC 60093
Dielectric Constant  3.2
@Frequency 1000 Hz,
Temperature 23.0 °C
3.2
@Frequency 1000 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength  23.0 kV/mm
@Thickness 2.00 mm
584 kV/in
@Thickness 0.0787 in
IEC 60243-1
Dissipation Factor  0.0050
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.0050
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Comparative Tracking Index  150 V 150 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear  45.0 µm/m-°C
@Temperature <=152 °C
25.0 µin/in-°F
@Temperature <=306 °F
Average below Tg; ISO 11359
  110 µm/m-°C
@Temperature >=152 °C
61.1 µin/in-°F
@Temperature >=306 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow   20.0 µm/m-°C
@Temperature <=152 °C
11.1 µin/in-°F
@Temperature <=306 °F
Below Tg; ISO 11359
  25.0 µm/m-°C
@Temperature >=152 °C
13.9 µin/in-°F
@Temperature >=306 °F
Above Tg; ISO 11359
Thermal Conductivity   0.300 W/m-K
@Temperature 23.0 °C
2.08 BTU-in/hr-ft²-°F
@Temperature 73.4 °F
Average; ISO/CD 22007-4
  0.350 W/m-K
@Temperature 23.0 °C
2.43 BTU-in/hr-ft²-°F
@Temperature 73.4 °F
Along flow; ISO 22007-4
Melting Point  373 °C 703 °F ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)  360 °C 680 °F ISO 75-f
Glass Transition Temp, Tg  152 °C 306 °F Onset; ISO 11357
  160 °C 320 °F Midpoint; ISO 11357
Glow Wire Test  960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 60695-2-12
 
Processing Properties Metric English Comments
Processing Temperature  <= 100 °C <= 212 °F Hopper Temperature
Nozzle Temperature  395 °C 743 °F  
Mold Temperature  190 - 215 °C 374 - 419 °F  
Drying Temperature   120 °C
@Time 18000 sec
248 °F
@Time 5.00 hour
 
  150 °C
@Time 10800 sec
302 °F
@Time 3.00 hour
 

.0..

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com


转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41514.html

免责声明: 本文 VICTREX PEEK®HT的™22gl30聚醚酮,30%玻璃纤维增强 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4