| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | Crystalline; ISO 1183 | ||
| Water Absorption at Saturation | 0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 | ||
| 0.75 % @Temperature 100 °C |
0.75 % @Temperature 212 °F |
immersion; ISO 62-1 | |||
| Viscosity | 200000 cP @Temperature 400 °C |
200000 cP @Temperature 752 °F |
melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | 395°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 20.0 cm @Thickness 1.00 mm |
7.87 in @Thickness 0.0394 in |
395°C nozzle, 200°C tool | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 @Temperature 23.0 °C |
86 @Temperature 73.4 °F |
ISO 868 | ||
| Tensile Strength, Yield | 115 MPa @Temperature 23.0 °C |
16700 psi @Temperature 73.4 °F |
ISO 527 | ||
| Elongation at Break | 25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
ISO 527 | ||
| Tensile Modulus | 4.30 GPa @Temperature 23.0 °C |
624 ksi @Temperature 73.4 °F |
ISO 527 | ||
| Flexural Strength | 16.0 MPa @Temperature 275 °C |
2320 psi @Temperature 527 °F |
ISO 178 | ||
| 32.0 MPa @Temperature 175 °C |
4640 psi @Temperature 347 °F |
ISO 178 | |||
| 105 MPa @Temperature 125 °C |
15200 psi @Temperature 257 °F |
ISO 178 | |||
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
ISO 178 | |||
| 130 MPa @Strain 3.50 %, Temperature 23.0 °C |
18900 psi @Strain 3.50 %, Temperature 73.4 °F |
ISO 178 | |||
| Flexural Modulus | 4.00 GPa @Temperature 23.0 °C |
580 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Compressive Strength | 30.0 MPa @Temperature 200 °C |
4350 psi @Temperature 392 °F |
ISO 604 | ||
| 90.0 MPa @Temperature 120 °C |
13100 psi @Temperature 248 °F |
ISO 604 | |||
| 140 MPa @Temperature 23.0 °C |
20300 psi @Temperature 73.4 °F |
ISO 604 | |||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/U | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/U | ||
| Charpy Impact, Notched | 0.380 J/cm² @Temperature 23.0 °C |
1.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm @Temperature 275 °C |
1.00e+9 ohm-cm @Temperature 527 °F |
IEC 60093 | ||
| 1.00e+15 ohm-cm @Temperature 125 °C |
1.00e+15 ohm-cm @Temperature 257 °F |
IEC 60093 | |||
| 1.00e+16 ohm-cm @Temperature 23.0 °C |
1.00e+16 ohm-cm @Temperature 73.4 °F |
IEC 60093 | |||
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
IEC 60243-1 | ||
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 55.0 µm/m-°C @Temperature <=152 °C |
30.6 µin/in-°F @Temperature <=306 °F |
Average below Tg; ISO 11359 | ||
| 130 µm/m-°C @Temperature >=152 °C |
72.2 µin/in-°F @Temperature >=306 °F |
Average above Tg; ISO 11359 | |||
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature <=152 °C |
25.0 µin/in-°F @Temperature <=306 °F |
Below Tg; ISO 11359 | ||
| 75.0 µm/m-°C @Temperature >=152 °C |
41.7 µin/in-°F @Temperature >=306 °F |
Above Tg; ISO 11359 | |||
| Thermal Conductivity | 0.290 W/m-K @Temperature 23.0 °C |
2.01 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 | ||
| 0.320 W/m-K @Temperature 23.0 °C |
2.22 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Along flow; ISO 22007-4 | |||
| Melting Point | 373 °C | 703 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ISO 75-f | ||
| Glass Transition Temp, Tg | 152 °C | 306 °F | Onset; ISO 11357 | ||
| 160 °C | 320 °F | Midpoint; ISO 11357 | |||
| Oxygen Index | 24 % @Thickness 0.400 mm |
24 % @Thickness 0.0157 in |
ISO 4239 | ||
| 35 % @Thickness 3.20 mm |
35 % @Thickness 0.126 in |
ISO 4239 | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature | ||
| Nozzle Temperature | 395 °C | 743 °F | |||
| Mold Temperature | 190 - 215 °C | 374 - 419 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|||
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |
||||
| De |
|||||
| Toxicity Index | 0.074 | NES 713; CO content | |||
| 0.15 | NES 713; CO2 content | ||||
| 0.22 | NES 713; Total gases |
||||
.