| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |||
| Filler Content | 30 % | 30 % | |||
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | |||
| Elongation at Break | 1.8 % | 1.8 % | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | |||
| Flexural Yield Strength | 200 MPa | 29000 psi | |||
| Flexural Modulus | 9.80 GPa | 1420 ksi | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | |||
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | |||
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
| Dielectric Constant | 3.1 | 3.1 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D145 | ||
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 | ||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 | ||
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | IEC 60112 | ||
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 1.50 mm |
60 - 120 sec @Thickness 0.0591 in |
UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
|||
| CTE, linear, Transverse to Flow | 44.0 µm/m-°C | 24.4 µin/in-°F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |||
| UL RTI, Electrical | 120 °C | 248 °F | UL746B | ||
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL746B | ||
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish | |||
| De |
|||||
| Comments | Optimized for heat & chemical resistance | ||||
.