日本出光/EA 537 SPS,30%玻璃填充

日本出光/EA 537 SPS,30%玻璃填充 类别:聚合物;热塑性的;聚苯乙烯(PS);间规聚苯乙烯(SPS);间规聚苯乙烯(SPS)与玻璃纤维或碳纤维 材质说明:水晶高分子、玻璃填充、阻燃、冲击改性。用于电子和电气应用
 物性表:

 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³  
Filler Content  30 % 30 %  
Water Absorption  0.010 % 0.010 % 24 hrs., 50% RH
Linear Mold Shrinkage, Flow  0.0010 - 0.0030 cm/cm 0.0010 - 0.0030 in/in  
Linear Mold Shrinkage, Transverse  0.0030 - 0.0070 cm/cm 0.0030 - 0.0070 in/in  
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  120 MPa 17400 psi  
Elongation at Break  2.0 % 2.0 %  
Tensile Modulus  11.6 GPa 1680 ksi  
Flexural Yield Strength  185 MPa 26800 psi  
Flexural Modulus  10.9 GPa 1580 ksi  
Izod Impact, Notched (ISO)  10.0 kJ/m² 4.76 ft-lb/in²  
Izod Impact, Unnotched (ISO)  28.0 kJ/m² 13.3 ft-lb/in²  
Charpy Impact Unnotched  3.20 J/cm² 15.2 ft-lb/in²  
Charpy Impact, Notched  1.00 J/cm² 4.76 ft-lb/in²  
 
Electrical Properties Metric English Comments
Electrical Resistivity  1.00e+16 ohm-cm 1.00e+16 ohm-cm  
Dielectric Constant  3.2 3.2  
Dielectric Strength  32.0 kV/mm 813 kV/in ASTM D145
Dissipation Factor  0.0020 0.0020 IEC 60250
Arc Resistance  60 - 120 sec 60 - 120 sec ASTM D495
Comparative Tracking Index  250 - 400 V 250 - 400 V IEC 60112
Hot Wire Ignition, HWI  30 - 60 sec
@Thickness 1.50 mm
30 - 60 sec
@Thickness 0.0591 in
UL 746A
High Amp Arc Ignition, HAI  >= 120 arcs
@Thickness 1.50 mm
>= 120 arcs
@Thickness 0.0591 in
UL 746A
High Voltage Arc-Tracking Rate, HVTR  >= 150 mm/min >= 5.91 in/min UL746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  15.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
8.33 µin/in-°F
@Temperature -22.0 - 86.0 °F
 
CTE, linear, Transverse to Flow  47.0 µm/m-°C 26.1 µin/in-°F  
Deflection Temperature at 0.46 MPa (66 psi)  265 °C 509 °F  
Deflection Temperature at 1.8 MPa (264 psi)  240 °C 464 °F  
UL RTI, Electrical  125 °C 257 °F UL746B
UL RTI, Mechanical with Impact  120 °C 248 °F UL746B
UL RTI, Mechanical without Impact  120 °C 248 °F UL746B
Flammability, UL94   V-0
@Thickness 0.750 mm
V-0
@Thickness 0.0295 in
 
  V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
 
  5VA
@Thickness 1.50 mm
5VA
@Thickness 0.0591 in
 
  5VA
@Thickness 2.30 mm
5VA
@Thickness 0.0906 in
 
 
Processing Properties Metric English Comments
Melt Temperature  280 - 310 °C 536 - 590 °F  
Mold Temperature  50.0 - 80.0 °C 122 - 176 °F  
  130 - 155 °C 266 - 311 °F For optimal surface finish
 
Descriptive Properties
Comments ISO10993  
  Thin wall V0 & 5VA


.0..
上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41536.html

免责声明: 本文 日本出光/EA 537 SPS,30%玻璃填充 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4