| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.13
|
--
|
g/cm³
|
ISO 1183 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
8.5
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.8
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
3300
|
1600
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Yield)
|
80.0
|
--
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Yield)
|
3.5
|
--
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break
|
--
|
> 50
|
%
|
ISO 527-2 |
|
Flexural Strength
|
115
|
75.0
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
3.0
|
--
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (23°C)
|
No Break
|
--
|
|
ISO 179/1eU |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
210
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
80.0
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
> 200
|
--
|
°C
|
ISO 306/B |
|
Melting Temperature
|
250 to 255
|
--
|
°C
|
ISO 11357-3 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+14
|
1.0E+12
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohm·cm
|
IEC 60093 |
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
1.60 mm
|
V-2
|
--
|
|
|
|
3.20 mm
|
V-2
|
--
|
|
| Injection |
Dry
|
Unit
|
|
|
Drying Temperature
|
80.0
|
°C
|
|
|
Drying Time
|
2.0 to 20
|
hr
|
|
|
Processing (Melt) Temp
|
280 to 300
|
°C
|
|
|
Mold Temperature
|
40.0 to 60.0
|
°C
|