Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Processing Method
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.10
|
--
|
g/cm³
|
ISO 1183 |
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
2200
|
950
|
MPa
|
ISO 527-2 |
|
Tensile Stress
|
ISO 527-2 | |||
|
Yield
|
57.0
|
35.0
|
MPa
|
|
|
Break
|
47.0
|
43.0
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2 | |||
|
Yield
|
4.4
|
19
|
%
|
|
|
Break
|
40
|
200
|
%
|
|
|
Flexural Modulus
|
1950
|
850
|
MPa
|
ISO 178 |
|
Flexural Strength
|
65.0
|
25.0
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-20°C
|
35
|
--
|
kJ/m²
|
|
|
23°C
|
60
|
100
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength (23°C)
|
No Break
|
--
|
|
ISO 179/1eU |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
> 200
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
70.0
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
> 200
|
--
|
°C
|
ISO 306/B |
|
Melting Temperature
|
260 to 265
|
--
|
°C
|
ISO 11357-3 |
| Injection |
Dry
|
Unit
|
|
|
Drying Temperature - Desiccant Dryer
|
80.0
|
°C
|
|
|
Drying Time - Desiccant Dryer
|
2.0 to 12
|
hr
|
|
|
Suggested Max Moisture
|
< 0.15
|
%
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
40.0 to 80.0
|
°C
|