Ultramid® A3Z HP|PA66|BASF物性表报告及物性特性介绍,Ultramid® A3Z HP|PA66|BASF注塑参数详情-塑料物性表查询网

Product TextsImpact-modified and stabilized injection moulding grade for components and housing with good low temperature impact resistance.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	1900 / -	MPa	ISO 527-1/-2
屈服应力(Yield stress)	50 / -	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5 / -	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	45 / -	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N / -	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	90 / -	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	28 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	262 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	64 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	170 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1070 / -	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingRegional AvailabilityNorth AmericaOther text informationInjection moldingMax. Water content: 0.20%If drying Drying time is 35 MPa (0-50 psi)Packing pressure affects It should be applied and maintained DisclaimerCopyright M-Base .