Product TextsUltramid® 8231G HS is a heat stabilized, 15% glass fiber reinforced Polyamid 6 injection molding compound. It is also available in non-heat stabilizedand/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	5960 / 2640	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	140 / 80	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	4 / 9	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	40 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	6.5 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	195 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	217 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	39 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	78 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.6 / -	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3.4 / -	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	0.01 / -	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	0.02 / -	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093
相比漏电起痕指数(Comparative tracking index)	- / 400	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	8.1 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2.3 / *	%	Sim. to ISO 62
密度(Density)	1230 / *	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1070	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.23	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	2730	J/(kg K)	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

Diagrams Water content: 0.15% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .