- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.934
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 19 % | 19 % | |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.00 MPa | 580 psi | ASTM D882 Method A |
| Film Tensile Strength at Yield, TD | 4.00 MPa | 580 psi | ASTM D882 Method A |
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 Method A |
| Film Elongation at Break, TD | 610 % | 610 % | ASTM D882 Method A |
| Dart drop Test | 260 g | 0.573 lb | Thickness not specified; ASTM D1709 Method A |
| Film Tensile Strength at Break, MD | 15.0 MPa | 2180 psi | ASTM D882 Method A |
| Film Tensile Strength at Break, TD | 13.0 MPa | 1890 psi | ASTM D882 Method A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | ASTM D3417 |
| Vicat Softening Point | 51.0 °C | 124 °F | ASTM D1525 |