- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.938
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.00 MPa | 580 psi | ASTM D882 Method A |
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ASTM D882 Method A |
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 Method A |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 Method A |
| Dart drop Test | 700 g | 1.54 lb | Thickness not specified; ASTM D1709 Method A |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 Method A |
| Film Tensile Strength at Break, TD | 27.0 MPa | 3920 psi | ASTM D882 Method A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | ASTM D3417 |
| Vicat Softening Point | 59.0 °C | 138 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 51 % | 51 % | 45° Gloss, ASTM D2457 |