- 拉伸强度 [MPa]: 14.5
- 弯曲模量 [MPa]: 0.0593
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ASTM D792 |
| Vinyl Acetate Content | 15 % | 15 % | by weight |
| Melt Index of Compound | 6.0 - 8.0 g/10 min | 6.0 - 8.0 g/10 min | 2.16/190; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | 2"/min; ASTM D638 |
| Elongation at Break | 700 % | 700 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.0593 GPa | 8.60 ksi | at 1% secant modulus; ASTM D790 |