- 熔体流动速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 4.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 23.5 - 26.5 % | 23.5 - 26.5 % | |
| Melt Flow | 5.5 - 9.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.5 - 9.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 29.2 | 29.2 | ISO 868 |
| Tensile Strength at Break | 25.9 MPa | 3760 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 4.20 MPa | 609 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 730 % | 730 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0264 GPa | 3.83 ksi | ISO R527 |
| Dart drop Test | 400 g | 0.882 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 77.0 °C | 171 °F | D.S.C. method |
| Vicat Softening Point | 55.0 °C | 131 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.6 % | 4.6 % | 50 micron film; ASTM D1003 |