- 熔体流动速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.931
- 弯曲强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.101
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505, ASTM D1928 Proc A | ||
| Vinyl Acetate Content | 9.0 % | 9.0 % | |||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 190/2.16 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 96 | 96 | ASTM D2240 | ||
| Hardness, Shore D | 43 | 43 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 Type IV | ||
| Elongation at Break | 685 % | 685 % | ASTM D638 Type IV | ||
| Flexural Modulus | 0.101 GPa | 14.6 ksi | 1% secant, ASTM D790 Method I | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 101 °C | 214 °F | ASTM D3417 | ||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 | ||
| Brittleness Temperature | -85.0 °C | -121 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Process | Extrusion | ||||
| Injection Molding | |||||
| region | US & Canada | ||||