- 熔体流动速率 [g/10min]: 3.3
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 6.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 8.0 - 9.5 % | 8.0 - 9.5 % | |
| Melt Flow | 3.3 - 4.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.3 - 4.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 38.6 | 38.6 | ISO 868 |
| Tensile Strength at Break | 20.6 MPa | 2990 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 6.50 MPa | 943 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 555 % | 555 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0695 GPa | 10.1 ksi | ISO R527 |
| Dart drop Test | 355 g | 0.783 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 100 °C | 212 °F | D.S.C. method |
| Vicat Softening Point | 77.0 °C | 171 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.6 % | 7.6 % | 50 micron film; ASTM D1003 |