- 熔体流动速率 [g/10min]: 55.0
- 密度 [g/cm3]: 0.962
- 弯曲模量 [MPa]: 0.00190
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 40 % | 40 % | AT Plastics PTM-39 |
| Melt Flow | 55 g/10 min @Load 2.16 kg, Temperature 190 °C | 55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 53 | 53 | ASTM D2240 |
| Tensile Strength at Break | 5.00 MPa | 725 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | >= 1150 % | >= 1150 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.00190 GPa | 0.276 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 52.0 °C | 126 °F | DSC; ASTM D3417 |
| Ring & Ball Softening Point | 107 °C | 225 °F | ASTM E28 |