- 熔体流动速率 [g/10min]: 600.0
- 密度 [g/cm3]: 0.931
- 弯曲模量 [MPa]: 0.0260
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 19 % | 19 % | AT Plastics PTM-39 |
| Melt Flow | 600 g/10 min @Load 0.325 kg, Temperature 125 °C | 600 g/10 min @Load 0.716 lb, Temperature 257 °F | Modified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Tensile Strength at Break | 3.50 MPa | 508 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 540 % | 540 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Ring & Ball Softening Point | 87.0 °C | 189 °F | ASTM E28 |