- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505; ASTM D1928 Proc A | ||
| Vinyl Acetate Content | 18 % | 18 % | AT Plastics PTM-39 | ||
| Thickness | 130 microns | 5.12 mil | |||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 4.00 MPa | 580 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 4.00 MPa | 580 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Elongation at Break, MD | 420 % | 420 % | Method A (500 mm/min); ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | Method A (500 mm/min); ASTM D882 | ||
| Dart Drop | >= 30.0 g/micron | >= 762 g/mil | f50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Tensile Strength at Break, TD | 27.0 MPa | 3920 psi | Method A (500 mm/min); ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 85.0 °C | 185 °F | DSC; ASTM D3417 | ||
| Vicat Softening Point | 61.0 °C | 142 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003 | ||
| Gloss | 50 % | 50 % | 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| Process | Film | ||||
| region | US & Canada | ||||