- 密度 [g/cm3]: 0.931
- 拉伸强度 [MPa]: 7.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 8.0 - 9.0 % | 8.0 - 9.0 % | |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 1.7 - 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.7 - 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D638 |
| Film Elongation at Break, MD | 485 % | 485 % | ASTM D882 |
| Film Elongation at Break, TD | 725 % | 725 % | ASTM D882 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Secant Modulus, MD | 0.0670 GPa | 9.72 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.0640 GPa | 9.28 ksi | 5%; ASTM D882 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 100 °C | 212 °F | ASTM D3418 |
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.8 % | 1.8 % | ASTM D1003 |
| Gloss | 140 % | 140 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Plasticizing Zone |
| 145 - 165 °C | 293 - 329 °F | Mixture Zone | |
| Feed Temperature | 135 - 140 °C | 275 - 284 °F | |
| Adapter Temperature | 165 - 185 °C | 329 - 365 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |