- 密度 [g/cm3]: 0.934
- 拉伸强度 [MPa]: 5.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 11 - 13 % | 11 - 13 % | |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.30 - 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 - 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D638 |
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 |
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 |
| Elongation at Break | 660 % | 660 % | ASTM D638 |
| Secant Modulus, MD | 0.0530 GPa | 7.69 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.0550 GPa | 7.98 ksi | 5%; ASTM D882 |
| Elmendorf Tear Strength, MD | 28.0 g/micron | 711 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.90 g/micron | 150 g/mil | ASTM D1922 |
| Dart drop Test | 425 g | 0.937 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 96.0 °C | 205 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.7 % | 1.7 % | ASTM D1003 |
| Gloss | 132 % | 132 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 155 °C | 284 - 311 °F | Plasticizing Zone |
| 155 - 170 °C | 311 - 338 °F | Mixture Zone | |
| Feed Temperature | 140 - 150 °C | 284 - 302 °F | |
| Adapter Temperature | 170 - 190 °C | 338 - 374 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |