- 密度 [g/cm3]: 0.951
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 0.0160
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 28 % | 28 % | TGA | ||
| Melt Index of Compound | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | ASTM D2240 | ||
| Hardness, Shore D | 35 | 35 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 4.20 MPa @Temperature 49.0 °C | 609 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 51.0 MPa @Temperature -20.0 °C | 7400 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 750 % | 750 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 500 % @Temperature -20.0 °C | 500 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 800 % @Temperature 49.0 °C | 800 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0190 GPa | 2.76 ksi | |||
| 0.0550 GPa @Temperature -20.0 °C | 7.98 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0160 GPa | 2.32 ksi | ASTM D790 | ||
| 0.00970 GPa @Temperature 49.0 °C | 1.41 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.0860 GPa @Temperature -20.0 °C | 12.5 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 19.0003 MPa | 2755.76 psi | |||
| 55.001 MPa @Temperature -20.0 °C | 7977.2 psi @Temperature -4.00 °F | ||||
| Tensile Impact Strength | 715 kJ/m² | 340 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 945 kJ/m² | 450 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 49 % | 49 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 100 % @Temperature 70.0 °C | 100 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 49.0 °C | 120 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 28 wt.% | ||||