- 密度 [g/cm3]: 0.93
- 弯曲强度 [MPa]: 19.0
- 弯曲模量 [MPa]: 0.110
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 15 % | 15 % | TGA | ||
| Melt Index of Compound | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 98 | 98 | ASTM D2240 | ||
| Hardness, Shore D | 47 | 47 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 12.0 MPa @Temperature 49.0 °C | 1740 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 32.0 MPa @Temperature -20.0 °C | 4640 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 650 % | 650 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 500 % @Temperature -20.0 °C | 500 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 750 % @Temperature 49.0 °C | 750 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0960 GPa | 13.9 ksi | |||
| 0.345 GPa @Temperature -20.0 °C | 50.0 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.110 GPa | 16.0 ksi | ASTM D790 | ||
| 0.0530 GPa @Temperature 49.0 °C | 7.69 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.503 GPa @Temperature -20.0 °C | 73.0 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 96.00 MPa | 13920 psi | |||
| 345.005 MPa | 50038.8 psi | ||||
| Tensile Impact Strength | 425 kJ/m² | 202 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 450 kJ/m² | 214 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 52 % | 52 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 84 % @Temperature 70.0 °C | 84 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 80.0 °C | 176 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 15 wt.% | ||||