- 熔体流动速率 [g/10min]: 0.47
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.938 g/cc | 0.938 g/cc | ISO 1183 |
| Vinyl Acetate Content | 17 % | 17 % | Internal Method |
| Thickness | 50.0 - 200 microns | 1.97 - 7.87 mil | Recommended |
| Melt Flow | 0.47 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.47 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 90 | 90 | ISO 868/A |
| Hardness, Shore D | 39 | 39 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 5.00 MPa | 725 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 4.50 MPa | 653 psi | ISO 527-3 |
| Film Elongation at Break, MD | 490 % | 490 % | ISO 527-3 |
| Film Elongation at Break, TD | 630 % | 630 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 3.057 g/micron | 77.65 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 5.095 g/micron | 129.4 g/mil | ISO 6383-2 |
| Dart drop Test | >= 700 g | >= 1.54 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 88.0 °C | 190 °F | Internal Method |
| Vicat Softening Point | 67.0 °C @Load 1.00 kg | 153 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ISO 14782 |
| Gloss | 72 % | 72 % | 45°; ASTM D2457 |