- 密度 [g/cm3]: 0.948
- 弯曲强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.0260
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 25 % | 25 % | TGA | ||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 87 | 87 | ASTM D2240 | ||
| Hardness, Shore D | 36 | 36 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 5.50 MPa @Temperature 49.0 °C | 798 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 45.0 MPa @Temperature -20.0 °C | 6530 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 800 % | 800 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 500 % @Temperature -20.0 °C | 500 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 900 % @Temperature 49.0 °C | 900 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0260 GPa | 3.77 ksi | |||
| 0.0760 GPa @Temperature -20.0 °C | 11.0 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0260 GPa | 3.77 ksi | ASTM D790 | ||
| 0.0170 GPa @Temperature 49.0 °C | 2.47 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.0860 GPa @Temperature -20.0 °C | 12.5 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 26.0004 MPa | 3771.04 psi | |||
| 76.00 MPa | 11020 psi | ||||
| Tensile Impact Strength | 590 kJ/m² | 281 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 880 kJ/m² | 419 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 49 % | 49 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 100 % @Temperature 70.0 °C | 100 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 53.0 °C | 127 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 25 wt.% | ||||