- 熔体流动速率 [g/10min]: 6.0
- 拉伸强度 [MPa]: 2.7
- 弯曲模量 [MPa]: 0.0150
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.952 g/cc | 0.952 g/cc | ISO 1183 |
| Vinyl Acetate Content | 28 % | 28 % | Internal Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | ISO 868/A |
| Hardness, Shore D | 31 | 31 | ISO 868/A |
| Tensile Strength, Yield | 2.70 MPa | 392 psi | ISO 527 |
| Flexural Modulus | 0.0150 GPa | 2.18 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 73.0 °C | 163 °F | Internal Method |
| Vicat Softening Point | 45.0 °C @Load 1.00 kg | 113 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |