- 熔体流动速率 [g/10min]: 3.2
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Vinyl Acetate Content | 9.0 % | 9.0 % | |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 3.2 g/10 min | 3.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 94 | 94 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 6.23 MPa | 904 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 5.81 MPa | 843 psi | ASTM D882 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Yield, MD | 9.0 % | 9.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 11 % | 11 % | ASTM D882 |
| Dart Drop | 7.95 g/micron | 202 g/mil | F50; ASTM D4272 |
| Film Tensile Strength at Break, MD | 25.9 MPa | 3750 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.9 MPa | 2740 psi | ASTM D882 |
| 1% Secant Modulus, MD | 84.8 MPa | 12300 psi | ASTM D882 |
| 1% Secant Modulus, TD | 91.0 MPa | 13200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 80.0 °C | 176 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | <= 221 °C | <= 430 °F | |