- 熔体流动速率 [g/10min]: 9.5
- 密度 [g/cm3]: 0.926
- 弯曲模量 [MPa]: 0.0931
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Particle Size | 5.0 - 50 µm | 5.0 - 50 µm | Spherical shape, 5-50 micron distribution. ETM = Equistar Test Method; ETM Malvern |
| Maximum Moisture Content | 0.10 | 0.10 | ETM 156 |
| Melt Flow | 9.5 g/10 min | 9.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 |
| Elongation at Break | 675 % | 675 % | ASTM D638 |
| Flexural Modulus | 0.0931 GPa | 13.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 96.0 °C | 205 °F | ASTM D3418 |
| Vicat Softening Point | 75.0 °C | 167 °F | ASTM D1525 |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |