- 熔体流动速率 [g/10min]: 0.5
- 脆化温度 [℃]: -76.0
- 透光率 [%]: 78.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 85.3 g/m²/day | 5.49 g/100 in²/day | ASTM F372 |
| Oxygen Transmission Rate | 8900 cc/m²/day | 573 cc/100 in²/day | ASTM D3985 |
| Vinyl Acetate Content | 13.5 % | 13.5 % | |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Antiblock Level | 15000 ppm | 15000 ppm | |
| Slip Level | 0.000 ppm | 0.000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.62 MPa | 960 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 5.52 MPa | 800 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Yield, MD | 18 % | 18 % | ASTM D882 |
| Film Elongation at Yield, TD | 16 % | 16 % | ASTM D882 |
| Elmendorf Tear Strength MD | 92 g | 92 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 128 g | 128 g | ASTM D1922 |
| Dart Drop | 15.0 g/micron | 380 g/mil | ASTM D4272 |
| Film Tensile Strength at Break, MD | 30.5 MPa | 4430 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.8 MPa | 4320 psi | ASTM D882 |
| 1% Secant Modulus, MD | 90.3 MPa | 13100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 91.0 MPa | 13200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 34.7 °C | 94.4 °F | DSC |
| Vicat Softening Point | 80.0 °C | 176 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Gloss | 88 % | 88 % | 45°; ASTM D2457 |
| Transmission, Visible | 78 % | 78 % | NAS; ASTM D1746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 216 °C | 420 °F | |
| Die Opening | 0.0635 cm | 0.0250 in | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |