- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 2.0 % | 2.0 % | ExxonMobil Method | ||
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 6000 ppm | 6000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.96 MPa | 1300 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.27 MPa | 1200 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 6.30 g/micron | 160 g/mil | ASTM D1922 | ||
| Dart Drop | 9.45 g/micron | 240 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.1 MPa | 3200 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 152 MPa | 22000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 193 MPa | 28000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 225 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 20 % | 20 % | ASTM D1003 | ||
| Gloss | 40 % | 40 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||