- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 5.0 % | 5.0 % | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 5050 ppm | 5050 ppm | |||
| Slip Level | 1500 ppm | 1500 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.45 MPa | 1080 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.10 MPa | 1030 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 | ||
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.1 % | 7.1 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.8 % | 5.8 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 | ||
| Dart drop Test | 180 g | 0.397 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.9 MPa | 3320 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.3 MPa | 3240 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 128 MPa | 18500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 144 MPa | 20900 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 103 °C | 217 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 89.0 °C | 192 °F | ExxonMobil Method | ||
| Vicat Softening Point | 84.4 °C | 184 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.4 % | 7.4 % | ASTM D1003 | ||
| Gloss | 70 % | 70 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||