- 密度 [g/cm3]: 0.951
- 弯曲模量 [MPa]: 0.0283
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 26.7 % | 26.7 % | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 76 | 76 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 27 | 27 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 8.27 MPa | 1200 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.0283 GPa | 4.10 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 19.0 J | 14.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 | ||
| 29.8 J | 22.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 72.8 °C | 163 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 46.1 °C | 115 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||