- 熔体流动速率 [g/10min]: 3.1
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 29.5 % | 29.5 % | ExxonMobil Method | ||
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 | ||
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.787 g/micron | 20.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 8.86 g/micron | 225 g/mil | ASTM D1922 | ||
| Dart Drop | 5.51 g/micron | 140 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 24.8 MPa | 3600 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 71.1 °C | 160 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 46.1 °C | 115 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.9 % | 3.9 % | ASTM D1003 | ||
| Gloss | 74 % | 74 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.