- 熔体流动速率 [g/10min]: 112.0
- 密度 [g/cm3]: 0.941
- 弯曲模量 [MPa]: 0.0314
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 24 % | 24 % | ExxonMobil Method |
| Melt Flow | 112 g/10 min | 112 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | 15s; ASTM D2240 |
| Hardness, Shore D | 23 | 23 | 15s; ASTM D2240 |
| Tensile Strength at Break | 3.52 MPa | 510 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Flexural Modulus | 0.0314 GPa | 4.55 ksi | 1% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 73.3 °C | 164 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 41.1 °C | 106 °F | ASTM D1525 |